Thermal expansion of Ti-substituted barium hexaferrite

P. Hernandez-Gomez, C. Francisco, de, V.A.M. Brabers, J.H.J. Dalderop

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

14 Citaten (Scopus)
156 Downloads (Pure)


Thermal expansion measurements in the range of 20–500 °C were carried out on both poly- and single crystalline samples of the hexagonal magnetoplumbite ferrite with composition BaTiFe11O19. The continuous scanning of the thermal expansion reveals the existence of a -type anomaly near the Curie temperature. In contrast to the usual observed anisotropic behavior for magnetoplumbite hexaferrites, the averaged thermal expansion coefficient for the a direction is larger than for the c direction, i.e., 12.8×10–6 and 9.5×10–6 °C–1, respectively.
Originele taal-2Engels
Pagina's (van-tot)3576-3578
TijdschriftJournal of Applied Physics
Nummer van het tijdschrift7
StatusGepubliceerd - 2000


Duik in de onderzoeksthema's van 'Thermal expansion of Ti-substituted barium hexaferrite'. Samen vormen ze een unieke vingerafdruk.

Citeer dit