The temperature dependence of the magnetization of magnetic multilayers

P.J.H. Bloemen, W.J.M. Jonge, de, F.J.A. Broeder, den

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

12 Citaten (Scopus)
1 Downloads (Pure)

Samenvatting

The magnetization of Co/Pt and Co/Au multilayers has been measured as a function of temperature. For the Co/Pt multilayers with fixed cobalt sublayer thickness of 4, 6 and 8 Å, the magnetization decreases faster with temperature as the platinum layers are made thicker. In contrast the magnetization of the Co/Au multilayers is nearly independent of the Au thickness in a range from 8 to 40 Å with a Co thickness of 6 Å and remain almost constant up to 500 K. Interlayer coupling and interdiffusion are discussed as possible causes for the observed behaviour.
Originele taal-2Engels
Pagina's (van-tot)105-108
Aantal pagina's4
TijdschriftJournal of Magnetism and Magnetic Materials
Volume93
DOI's
StatusGepubliceerd - 1991

Vingerafdruk

Duik in de onderzoeksthema's van 'The temperature dependence of the magnetization of magnetic multilayers'. Samen vormen ze een unieke vingerafdruk.

Citeer dit