The preparation of highly ordered single layer ZSM-5 coating on prefabricated stainless steel microchannels

E.V. Rebrov, G.B.F. Seijger, H.P.A. Calis, M.H.J.M. Croon, de, C.M. Bleek, van den, J.C. Schouten

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

121 Citaten (Scopus)
1 Downloads (Pure)

Samenvatting

An elegant way to prepare catalytically active microreactors is by applying a coating of zeolite crystals onto a metal microchannel structure. In this study the hydrothermal formation of ZSM-5 zeolitic coatings on AISI 316 stainless steel plates with a microchannel structure has been investigated at different synthesis mixture compositions. The procedures of coating and thermal treatment have also been optimized. Obtaining a uniform thickness of the coating within 0.5 mm wide microchannels requires a careful control of various synthesis variables. The role of these factors and the problems in the synthesis of these zeolitic coatings are discussed. In general, the synthesis is most sensitive to the H2O/Si ratio as well as to the orientation of the plates with respect to the gravity vector. Ratios of H2O/Si=130 and Si/template=13 were found to be optimal for the formation of a zeolitic film with a thickness of one crystal at a temperature of 130°C and a synthesis time of about 35 h. At such conditions, ZSM-5 crystals were formed with a typical size of 1.5 µm×1.5 µm×1.0 µm and a very narrow (within 0.2 µm) crystal size distribution. The prepared samples proved to be active in the selective catalytic reduction (SCR) of NO with ammonia. The activity tests have been carried out in a plate-type microreactor. The microreactor shows no mass transfer limitations and a larger SCR reaction rate is observed in comparison with pelletized Ce-ZSM-5 catalysts.
Originele taal-2Engels
Pagina's (van-tot)125-143
TijdschriftApplied Catalysis. A, General
Volume206
Nummer van het tijdschrift1
DOI's
StatusGepubliceerd - 2001

Vingerafdruk

Duik in de onderzoeksthema's van 'The preparation of highly ordered single layer ZSM-5 coating on prefabricated stainless steel microchannels'. Samen vormen ze een unieke vingerafdruk.

Citeer dit