The electrical properties of manganese ferrite (MnFe2O4) at the Neel temperature

T.E. Whall, N. Salerno, Y.G. Proykova, V.A.M. Brabers

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

10 Citaten (Scopus)

Samenvatting

Electrical conductivity and thermopower measurements have been made on zinc and manganese ferrous ferrite, ZnxFe3-xO4 and MnxFe3 -xO4 with 0 = X <1, in the temperature range 100–300 K. The results for X <0.5 are tentatively interpreted in terms of the formation of a Coulomb gap at low temperatures in an energy band of localized states. For X = 0.5 the electrical conductivity is symptomatic of nearest-neighbour hopping, and the thermopower varies as In c where c=(1 - X)/2. The energy bandwidth of conduction states has been extracted from the thermopower and electrical conductivity data and is shown to be roughly proportional to the standard deviation of the Zn and Mn distributions [X(1 - X)1/2. A polaron contribution to the conductivity activation energy of approximately 0.03 eV at room temperature has been deduced for Mn0.8Fe2.2O4 and Mn0.8Fe2.1O4.
Originele taal-2Engels
Pagina's (van-tot)99-105
TijdschriftPhilosophical Magazine B : physics of condensed matter, statistical mechanics, electronic, optical and magnetic properties
Volume56
Nummer van het tijdschrift1
DOI's
StatusGepubliceerd - 1987

Vingerafdruk Duik in de onderzoeksthema's van 'The electrical properties of manganese ferrite (MnFe2O4) at the Neel temperature'. Samen vormen ze een unieke vingerafdruk.

Citeer dit