Studies on the degradation of Li-ion batteries by the use of microreference electrodes

J. Zhou, P.H.L. Notten

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

53 Citaten (Scopus)
1 Downloads (Pure)

Samenvatting

Li-ion batteries made by the Lithylene technology were investigated after extensive cycling for a mechanistic understanding of the capacity fade phenomena. The batteries cycled 500 times at 0.5 C were found to lose 13% of their original capacity, which was solely due to the loss of active materials. The negative electrode maintained its capacity to contain Li+ ions from the positive electrode. The loss of positive electrode materials was attributed to formation and thickening of the surface layer and structure disorder evidenced by XRD measurements. In situ impedance measurements revealed that the positive electrode was also responsible for the impedance rise upon cycling. The charge transfer resistance was found to be the most influential factor in the battery impedance, which increased exponentially during cycling. This increase was proved not due to the decrease of positive electrode surface area but resulted from growth of the surface layer.
Originele taal-2Engels
Pagina's (van-tot)553-560
TijdschriftJournal of Power Sources
Volume177
Nummer van het tijdschrift2
DOI's
StatusGepubliceerd - 2008

Vingerafdruk

Duik in de onderzoeksthema's van 'Studies on the degradation of Li-ion batteries by the use of microreference electrodes'. Samen vormen ze een unieke vingerafdruk.

Citeer dit