Reliability and microstructure of lead-free solder joints in industrial electronics after accelerated thermal aging

F. Scaltro, M.H. Biglari, A. Kodentsov, O. Yakovleva, E. Brom

Onderzoeksoutput: Hoofdstuk in Boek/Rapport/CongresprocedureConferentiebijdrageAcademic

3 Downloads (Pure)

Samenvatting

The reliability of lead-free (LF) solder joints in surface-mounted device components (SMD) has been investigated after thermo-cycle testing. Kirkendall voids have been observed at the interface component/solder together with the formation of fractures. The evolution, the morphology and the elemental analysis of the intermetallic layer have been evaluated before and after the thermal treatment. Voids produced by the release of volatile species during the soldering process due to the application of flux were present. If compared with SnPb soldered systems, lead-free joints are characterized by larger and a higher amount of voids. In several electronic joints (ball grid arrays (BGA), surface-mounted device components (SMD), etc.) fractures developed after the thermal stresses generated during the accelerated thermal aging. Warpage of the PCB has also been observed. Backward and forward compatibility of SnPb and lead-free BGA connections has been performed on pads with an ENIG finish. The effect of the reflow peak temperature on the structure of the intermetallic layer has been assessed.
Originele taal-2Engels
TitelIPC APEX Expo 2009, 31 March - 2 April 2009, Las Vegas, Nevada
Plaats van productieBannockburn
UitgeverijIPC
Pagina's534-546
Volume1
ISBN van geprinte versie9781615670826
StatusGepubliceerd - 2009
Evenementconference; IPC APEX Expo 2009; 2009-03-31; 2009-04-02 -
Duur: 31 mrt. 20092 apr. 2009

Congres

Congresconference; IPC APEX Expo 2009; 2009-03-31; 2009-04-02
Periode31/03/092/04/09
AnderIPC APEX Expo 2009

Vingerafdruk

Duik in de onderzoeksthema's van 'Reliability and microstructure of lead-free solder joints in industrial electronics after accelerated thermal aging'. Samen vormen ze een unieke vingerafdruk.

Citeer dit