Polymer photovoltaic devices from stratified multilayers of donor-acceptor blends

L.C. Chen, D. Godovsky, O. Inganäs, J.C. Hummelen, R.A.J. Janssen, M. Svensson, M.R. Andersson

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

108 Citaten (Scopus)

Samenvatting

The conversion efficiencies of organic photovoltaic devices have been improved by a factor of 4-5 by introducing a large surface-area interface between the donor and acceptor layers. Stratified films of a fullerene-based acceptor (see Figure) were spin-coated on top of a donor (MDMO-PPV), forming a diffuse interface with unusual morphology that displayed high energy-conversion efficiencies.