Ostwald ripening on a planar Co/SiO2 catalyst exposed to model Fischer-Tropsch synthesis conditions

D. Kistamurthy, A.M. Saib, D.J. Moodley, J.W. Niemantsverdriet, C.J. Weststrate

    Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

    50 Citaten (Scopus)

    Samenvatting

    Catalyst deactivation is an important topic for industrial catalyst development. Sintering of small cobalt crystallites is one of the deactivation mechanisms of cobalt-based Fischer–Tropsch synthesis (FTS) catalysts. This study investigates the mechanism of cobalt sintering at low-conversion FTS conditions. A Co/SiO2/Si(1 0 0) model catalyst is exposed to 20 bar dry synthesis gas (H2/CO: 2/1) at 230 °C for 10 h. Cobalt nanoparticles were characterized before and after treatment using transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). TEM images of identical locations on the model catalyst showed a loss of some small crystallites and decrease in size of some crystallites. Sintering is dominated by an Ostwald ripening mechanism using our model catalyst under the present conditions. Complementary XPS measurements confirm the loss of Co dispersion. Therefore, the loss of small Co nanoparticles causes a rapid loss of metal surface area when exposed to model FTS conditions
    Originele taal-2Engels
    Pagina's (van-tot)123-129
    TijdschriftJournal of Catalysis
    Volume328
    DOI's
    StatusGepubliceerd - aug 2015

    Vingerafdruk

    Duik in de onderzoeksthema's van 'Ostwald ripening on a planar Co/SiO2 catalyst exposed to model Fischer-Tropsch synthesis conditions'. Samen vormen ze een unieke vingerafdruk.