Mn diffusion and the thermal stability of tunneling spin polarization

P.V. Paluskar, C.H. Kant, J.T. Kohlhepp, A.T. Filip, H.J.M. Swagten, B. Koopmans, W.J.M. Jonge, de

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

9 Citaten (Scopus)
78 Downloads (Pure)

Samenvatting

We examine the role of Mn diffusion in the thermal stability of tunneling spin polarization P by directly measuring P of Al/AlOx/Co/FeMn and Al/AlOx/Co90Fe10/FeMn junctions using superconducting tunneling spectroscopy (STS). We confirm Mn diffusion in our junctions using x-ray photoelectron spectroscopy after an ultrahigh vacuum 500 °C anneal. Surprisingly, and in contrast to the current belief, no drop in P is observed using STS. Therefore, though Mn diffuses significantly, it cannot be solely responsible for the drop in tunneling magnetoresistance observed after postdeposition anneals above 300 °C. ©2005 American Institute of Physics
Originele taal-2Engels
Artikelnummer10C925
Pagina's (van-tot)10C925-1/3
TijdschriftJournal of Applied Physics
Volume97
Nummer van het tijdschrift10, Pt. 2
DOI's
StatusGepubliceerd - 2005

Vingerafdruk Duik in de onderzoeksthema's van 'Mn diffusion and the thermal stability of tunneling spin polarization'. Samen vormen ze een unieke vingerafdruk.

  • Citeer dit