Luminescence properties of Eu2+ - activated alkaline-earth silicon-oxynitride MSi2O2-deltaN2+2/3delta (M = Ca, Sr, Ba) : A promising class of novel LED conversion phosphors

Y.Q. Li, A.C.A. Delsing, G. With, de, H.T.J.M. Hintzen

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

591 Citaten (Scopus)
4 Downloads (Pure)

Samenvatting

The luminescence properties of Eu2+-activated alk.-earth Si-oxynitrides were studied. In the BaO-SiO2-Si3N4 system, a new BaSi2O2N2 compd. was obtained having the monoclinic structure with lattice parameters a 14.070(4), b 7.276(2), c 13.181(3) .ANG., b 107.74(6)°. All MSi2O2-dN2+2/3d:Eu2+ (M = Ca, Sr, Ba) materials can be efficiently excited in the UV to visible region (370-460 nm), making them attractive as conversion phosphors for LED applications. A blue-green emission at 490-500 is obsd. for BaSi2O2N2:Eu2+, yellow emission at 560 nm for CaSi2O2-dN2+2/3d:Eu2+ (d » 0), and a green-yellow emission peaking from 530 to 570 nm for SrSi2O2-dN2+2/3d:Eu2+ (d » 1), the position depending on the exact value of d. BaSi2O2N2:Eu2+ is the most promising conversion phosphor for white-light LEDs due to its high conversion efficiency for blue light from InGaN-based LEDs related to its very small Stokes shift.
Originele taal-2Engels
Pagina's (van-tot)3242-3248
TijdschriftChemistry of Materials
Volume17
Nummer van het tijdschrift12
DOI's
StatusGepubliceerd - 2005

Vingerafdruk

Duik in de onderzoeksthema's van 'Luminescence properties of Eu2+ - activated alkaline-earth silicon-oxynitride MSi2O2-deltaN2+2/3delta (M = Ca, Sr, Ba) : A promising class of novel LED conversion phosphors'. Samen vormen ze een unieke vingerafdruk.

Citeer dit