Investigation of stick phenomena in metal-on-metal hip joints after resting periods

M.A. Wimmer, R. Nassult, C.M. Sprecher, J. Loos, G. Taeger, A. Fischer

Onderzoeksoutput: Hoofdstuk in Boek/Rapport/CongresprocedureConferentiebijdrageAcademic

27 Citaten (Scopus)

Samenvatting

Insufficient understanding of tribological behaviour in total joint arthroplasty is considered as one of the reasons for prosthesis failure. Contrary to the continuous motion input profiles of hip simulators, human locomotion contains motion interruptions. These occurring resting periods can cause stick phenomena in metal-on-metal hip joints. The aim of the present study was to investigate the tribological sensitivity of all-metal bearings to motion interruptions on in vitro test specimens and retrieved implants. Friction and wear with and without resting periods were quantified. Unlike the metal-on-polyethylene joints, the static friction of metal-on-metal joints increased up to µs = 0.3 with rest, while wear appeared to be unaffected. This effect is caused by the interlocking of firmly adhered carbon layers, which were generated from the protein-containing lubricant through tribochemical reactions. Since more than 80 per cent of the retrieved implants exhibited macroscopically visible carbon layers, the increase in friction presumably also occurs under physiological conditions, which is then transferred to the bone-implant interface. These recurrent tangential stress peaks should be considered for the design features of the cup-bone interface, in particular when larger-sized implant heads are used.
Originele taal-2Engels
TitelProceedings of the Institution of Mechanical Engineers: Part H: Journal of Engineering in Medicine
Pagina's219-227
DOI's
StatusGepubliceerd - 2006

Publicatie series

NaamJournal of Engineering in Medicine
VolumeH2

Vingerafdruk Duik in de onderzoeksthema's van 'Investigation of stick phenomena in metal-on-metal hip joints after resting periods'. Samen vormen ze een unieke vingerafdruk.

Citeer dit