Influence of material anisotropy on fatigue crack growth in C–Mn steels of existing structures

Henk Slot (Corresponding author), Monica Nicoreac, Johan Maljaars

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

5 Citaten (Scopus)
169 Downloads (Pure)


Rolled steel plates and sections are often applied in structures in such a way that the principal load direction corresponds with the rolling direction. Examples are beams, arches, or pylons of bridges, supporting beams of ship decks, and the main elements of crane structures. However, some types of structure are subjected to a multiaxial stress state or are loaded with the main load direction perpendicular to rolling. The orientation may influence the mechanical properties. This paper studies the influence of anisotropy observed in the microstructure of rolled C–Mn steels on the tensile properties, Charpy impact values and particularly the fatigue crack growth rates. The influence of anisotropy is determined through tests performed at different orientations with respect to the rolling direction, namely, L-T, T-L and T-S orientations. Samples were taken from structures that were constructed between 25 and 50 years ago from steel grades Fe510C or St52.3 (modern equivalences S355J2 or S355N). The orientation appears to have a statistically relevant influence on Charpy impact value and fatigue crack growth rate. The anisotropy ratio, defined as the ratio between the mechanical property in a certain orientation with that of the L-T orientation, ranged between 0.30 and 0.53 for Charpy impact values. The anisotropy ratios appear correlated with the absolute Charpy value, with a correlation coefficient of ρ = −0.8. The anisotropy ratios of the crack growth in T-L and T-S orientations were 1.19 and 0.43, respectively. Anisotropy ratios for crack growth appear uncorrelated with anisotropy ratios for Charpy impact. The observed anisotropy may partially explain the difference between uniaxial and multiaxial fatigue crack growth as determined by others.

Originele taal-2Engels
Pagina's (van-tot)2527-2541
Aantal pagina's15
TijdschriftFatigue and Fracture of Engineering Materials and Structures
Nummer van het tijdschrift11
Vroegere onlinedatum29 jun. 2020
StatusGepubliceerd - 1 nov. 2020


Duik in de onderzoeksthema's van 'Influence of material anisotropy on fatigue crack growth in C–Mn steels of existing structures'. Samen vormen ze een unieke vingerafdruk.

Citeer dit