Influence of interface structure on the tunnelling spin polarization of CoFeB alloys

P.V. Paluskar, J.T. Kohlhepp, H.J.M. Swagten, B. Koopmans, R. Wolters, H. Boeve, E. Snoeck

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

2 Citaten (Scopus)
3 Downloads (Pure)

Samenvatting

We present measurements of tunnelling spin polarization (TSP) of CoFeB alloys in Al/AlOx/CoFeB tunnel junctions using superconducting tunnelling spectroscopy. We observe that though Co72Fe20B8 (at.%) layers crystallize in the fcc structure, in junctions annealed above 300 DegC the measured TSP degrades, indicating that in these junctions the TSP of amorphous CoFeB is higher than its cryst. counterpart.
Originele taal-2Engels
Pagina's (van-tot)1234-1237
TijdschriftJournal of Physics D: Applied Physics
Volume40
Nummer van het tijdschrift5
DOI's
StatusGepubliceerd - 2007

Vingerafdruk Duik in de onderzoeksthema's van 'Influence of interface structure on the tunnelling spin polarization of CoFeB alloys'. Samen vormen ze een unieke vingerafdruk.

  • Citeer dit