High-pressureGd Mössbauer experiments on Gd intermetallic compounds compared with first-principles band-structure calculations

F. Mulder, R. Coehoorn, R. C. Thiel, K.H.J. Buschow

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

7 Citaten (Scopus)


High-pressure (Formula presented)Gd Mössbauer measurements on Gd metal, GdCo(Formula presented), GdRu(Formula presented)Si(Formula presented), and Gd(Formula presented)Co(Formula presented)N(Formula presented) were performed at 4.2 K. The maximum pressures reached were about 18 GPa. The resulting volume reductions of 20-30 % were determined using high-pressure x-ray diffraction. The pressure dependence of the electric-field gradients and hyperfine fields obtained for the first three systems was compared with predictions from first-principles band-structure calculations. Significant changes of the hyperfine parameters are observed, especially for elemental Gd metal. With increasing pressure, an increase of the electron density at the Gd nuclei is found in all compounds. The values of the hyperfine field initially increase with pressure. For Gd metal the induced structural phase transitions result in large changes in the electric-field gradient at the nucleus (Formula presented). The intermetallic compounds show no structural phase transitions and relatively small changes in (Formula presented) The combination of experiment and calculations indicates that the transition-metal magnetic moments decrease at high pressure. Although for zero pressure predictions of the electric-field gradient and the hyperfine fields, based on the calculations, are quite accurate, the calculated pressure dependence of the hyperfine parameters for Gd, GdCo(Formula presented), and GdRu(Formula presented)Si(Formula presented) does not in all cases lead to a satisfactory agreement with experiment. The application of pressures therefore may give additional stimulus for the improvement of the theoretical description of band structures and hyperfine parameters.

Originele taal-2Engels
Pagina's (van-tot)5786-5796
Aantal pagina's11
TijdschriftPhysical Review B - Condensed Matter and Materials Physics
Nummer van het tijdschrift10
StatusGepubliceerd - 1 jan 1997
Extern gepubliceerdJa


Duik in de onderzoeksthema's van 'High-pressureGd Mössbauer experiments on Gd intermetallic compounds compared with first-principles band-structure calculations'. Samen vormen ze een unieke vingerafdruk.

Citeer dit