High efficiency n-type silicon solar cells with front side boron emitter

J. Benick, B. Hoex, G. Dingemans, W.M.M. Kessels, A. Richter, M. Hermle, S.W. Glunz

Onderzoeksoutput: Hoofdstuk in Boek/Rapport/CongresprocedureConferentiebijdrageAcademic

Samenvatting

High-efficiency n-type PERL solar cells with a front side boron emitter passivated by ALD Al2O3 are presented within this work. For the applied PERL cell design two variations have been employed: i) different boron emitters (deep / shallow) and ii) different dielectric layers for rear side passivation (thermal grown SiO2 and PECVD SiNx). Both, thermal grown SiO2 as well as PECVD SiNx provide an effective passivation of the n-type rear surface with effective surface recombination velocities of 4 cm/s and 7 cm/s respectively. If the metalized rear side point contacts (with BSF) together with the recombination of the 1 O cm FZ base silicon are taken into account this results in saturation current densities of 30 fA/cm2 and 37 fA/cm2 respectively, limiting the open-circuit voltage (all recombination losses due to the front side are neglected) to 717 mV and 712 mV. The passivation of the boron emitter with ALD Al2O3 results in an emitter saturation current density as low as 11 fA/cm2. Together with the losses at the rear side as well as the front side contacts this allows for an open-circuit voltage of the applied PERL solar cell design of ~700 mV. For n-type PERL solar cells featuring a lowly doped boron emitter as well as a SiO2 passivated rear such a high open-circuit voltage (up to 703.6 mV) could be reached also at the device level, resulting in a conversion efficiency of 23.4%. Also for the PERL solar cells featuring a high surface concentration boron emitter with a PECVD SiNx passivated rear, i.e. first steps towards an industrial structure, still a high conversion efficiency of 21.8% could be achieved. All cells have been shown to be perfectly stable under illumination at 1 sun.
Originele taal-2Engels
TitelProceedings 24th European Photovoltaic Solar Energy Conference, 21-25 september 2009, Hamburg, Germany
Plaats van productieHamburg, Germany
Pagina's2BP.1.3-863/870
DOI's
StatusGepubliceerd - 2009
Evenement24th European Photovoltaic Solar Energy Conference (EU PVSEC 2004) - Hamburg
Duur: 21 sep 200925 sep 2009
Congresnummer: 24

Congres

Congres24th European Photovoltaic Solar Energy Conference (EU PVSEC 2004)
Verkorte titelPVSEC 2004
StadHamburg
Periode21/09/0925/09/09
Ander24th European Photovoltaic Solar Energy Conference (EU PVSEC), 21-25 September 2009, Hamburg, Germany

Vingerafdruk Duik in de onderzoeksthema's van 'High efficiency n-type silicon solar cells with front side boron emitter'. Samen vormen ze een unieke vingerafdruk.

Citeer dit