Fracture and strain rate behavior of airplane fuselage materials under blast loading

J. Mediavilla Varas, F. Soetens, E. Kroon, J.E. Aanhold, van, O.R. Meulen, van der, M. Sagimon

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

1 Citaat (Scopus)
106 Downloads (Pure)

Samenvatting

The dynamic behavior of three commonly used airplane fuselage materials is investigated, namely of Al2024-T3, Glare-3 and CFRP. Dynamic tensile tests using a servo-hydraulic and a light weight shock testing machine (LSM) have been performed. The results showed no strain rate effect on Al2024-T3 and an increase in the failure strain and failure strength of Glare-3, but no stiffening. The LSM results on CFRP were inconclusive. Two types of fracture tests were carried out to determine the dynamic crack propagation behavior of these materials, using prestressed plates and pressurized barrels, both with the help of explosives. The prestressed plates proved to be not suitable, whereas the barrel tests were quite reliable, allowing to measure the crack speeds. The tougher, more ductile materials, Al2024-T3 and Glare-3, showed lower crack speeds than CFRP, which failed in a brittle manner.
Originele taal-2Engels
Artikelnummer42017
Aantal pagina's8
TijdschriftEPJ Web of Conferences
Volume6
DOI's
StatusGepubliceerd - 2010

Vingerafdruk Duik in de onderzoeksthema's van 'Fracture and strain rate behavior of airplane fuselage materials under blast loading'. Samen vormen ze een unieke vingerafdruk.

  • Citeer dit

    Mediavilla Varas, J., Soetens, F., Kroon, E., Aanhold, van, J. E., Meulen, van der, O. R., & Sagimon, M. (2010). Fracture and strain rate behavior of airplane fuselage materials under blast loading. EPJ Web of Conferences, 6, [42017]. https://doi.org/10.1051/epjconf/20100642017