"Foil spintrusion" of high-performance polymer films

J. Lefèvre, K. Feldman, J. Giesbrecht, P. Smith, T.A. Tervoort, H.E.H. Meijer

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

6 Citaten (Scopus)

Samenvatting

This article describes the development of high-performance polymer foils by direct orientation in the liquid-crystalline phase of a thermotropic copolyester, based on p-hydroxybenzoic acid (HBA) and 2-hydroxy-6-naphthoic acid (HNA), better known under the trade name Vectra®. Application of a simple air-gap-filament-fusion-extrusion process ("foil spintrusion") with the use of a newly developed die, results in highly oriented free-standing foils, as thin as 3 µm. These foils have a mechanical performance that is comparable with those of commercially produced fibers of the same material. These uniaxially oriented foils could be laminated upon hot-compacting without, or with as little as 5 wt % of an adhesive, yielding planar foils as thin as 18 µm, which feature excellent isotropic, in-plane mechanical properties, that is, a Young's modulus E = 20 GPa and a tensile strength s = 0.5 GPa.
Originele taal-2Engels
Pagina's (van-tot)1713-1727
Aantal pagina's15
TijdschriftJournal of Polymer Science, Part B: Polymer Physics
Volume50
Nummer van het tijdschrift24
DOI's
StatusGepubliceerd - 2012

Vingerafdruk Duik in de onderzoeksthema's van '"Foil spintrusion" of high-performance polymer films'. Samen vormen ze een unieke vingerafdruk.

Citeer dit