Exchange anisotropy as a probe of antiferromagnetism in expanded face-centered-tetragonal Mn(001) layers

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

13 Citaten (Scopus)
82 Downloads (Pure)

Samenvatting

Manganese (Mn) grows coherent and with an expanded metastable face-centered-tetragonal (e-fct) structure on ultrathin fct Co(001)/Cu(001) template layers. From the temp. dependence of the obsd. unidirectional Mn/Co interface exchange anisotropy, an antiferromagnetic state with a blocking temp. around 410 K is found for a 21 monolayer thick e-fct Mn(001) film. The temp. dependent coercivity enhancement of the Co films, which is induced by the proximity of the antiferromagnetic Mn layer, suggests a Ne.acte.el temp. above 410 K for this Mn phase. [on SciFinder (R)]
Originele taal-2Engels
Artikelnummer032507
Pagina's (van-tot)032507-1/3
Aantal pagina's3
TijdschriftApplied Physics Letters
Volume89
Nummer van het tijdschrift3
DOI's
StatusGepubliceerd - 2006

Vingerafdruk Duik in de onderzoeksthema's van 'Exchange anisotropy as a probe of antiferromagnetism in expanded face-centered-tetragonal Mn(001) layers'. Samen vormen ze een unieke vingerafdruk.

  • Citeer dit