Electrical conductivity study of defects in zirconium doped yttrium aluminium garnet ceramics

L.H. Schuh, R. Metselaar, G. With, de

Onderzoeksoutput: Hoofdstuk in Boek/Rapport/CongresprocedureConferentiebijdrageAcademicpeer review

98 Downloads (Pure)

Samenvatting

High temperature measurements of conductivity as f(T) of Y3Al5O12 (YAG) doped with 50 ppm Zr in CO/CO2 and H2/H2O gas mixtures show a significant difference in the activation energy (3.54 resp. 1.91 eV) at constant oxygen partial pressure. The sign of the Seebeck coefficient indicates that a H2/H2O atmosphere introduces protons as conducting species into the garnet lattice. Impedance spectroscopy revealed that this is a bulk effect, while the grain boundaries are nearly unaffected by ambient atmosphere. Ionic and electronic conductivity as f(pO2) show that ionic conductivity dominates in the high pO2 regime, while at low pO2 electronic conductivityincreases with pO2-1/5 indicating that either singly or doubly ionised oxygen vacancies or defect clusters appear as prevailing ionic defects.
Originele taal-2Engels
TitelScience of ceramics : proceedings of the ... international conference, 14th, Canterbury, England, 7-9 September, 1987
RedacteurenD. Taylor
Plaats van productieStoke-on-Trent
UitgeverijThe Institute of Ceramics
Pagina's973-978
StatusGepubliceerd - 1988

Publicatie series

NaamScience of Ceramics
Volume14
ISSN van geprinte versie0080-7575

Vingerafdruk Duik in de onderzoeksthema's van 'Electrical conductivity study of defects in zirconium doped yttrium aluminium garnet ceramics'. Samen vormen ze een unieke vingerafdruk.

Citeer dit