Dielectric relaxation in vitreous borates at low temperatures

H.J.C.A. Quinten, W.J.T. van Gemert, J.M. Stevels

    Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

    8 Citaten (Scopus)

    Samenvatting

    Dielectric relaxation measurements have been made in vitreous alkali borates from 4.2 to 300 K, and from 102 to 105 s-1. Two types of relaxation are present: the first, at about 25 K (103 s-1), is intimately related to the presence of tetrahedral BO4 units in distorted positions, and the second, at about 160 K (103 s-1), is correlated with water that is present in small quantities in glass.