Characterization of thermal and electrical stability of MOCVD HfO 2-HfSiO4 dielectric layers with polysilicon electrodes for advanced CMOS technologies

Z.M. Rittersma, J.J.G.P. Loo, Y.V. Ponomarev, M.A. Verheijen, M. Kaiser, F. Roozeboom, S. van Elshocht, M. Caymax

Onderzoeksoutput: Bijdrage aan tijdschriftArtikel recenserenAcademicpeer review

11 Citaten (Scopus)

Samenvatting

The thermal and electrical stability of HfO2-HfSiO4 dielectric layers with polysilicon electrodes are investigated in view of their use as gate dielectrics in advanced complementary metal oxide semiconductor (CMOS) technologies. The layers were deposited on 1 nm silicon oxide layers using metallorganic chemical vapor deposition (MOCVD). In situ p-doped polysilicon electrodes were deposited using rapid thermal chemical vapor deposition and low pressure chemical vapor deposition, respectively. The influence of rapid thermal annealing and postdeposition annealing of the high-k layers was investigated using MOS capacitors. The lowest equivalent oxide thickness was around 19.3 Å with a leakage current reduction of approximately 1000 times as compared to SiO2. MOSFETs fabricated using a standard direct gate etch approach were used to study the stability of the dielectric and device properties as functions of activation anneal and implant conditions. A major problem was found to be the stability of the threshold voltage VT. After 50 consecutive Id-V g dc sweeps from -1 to +2 V, the threshold voltage of n-MOS devices shifted 50-200 mV. Using pulsed Id-Vg measurement technique, a hysteresis on the order of 300-400 mV was found. Only a minor improvement was achieved by different annealing of the layers. In conclusion, it was found that these layers exhibit unacceptably high instability to provide a solution as a gate dielectric for advanced CMOS technologies.

Originele taal-2Engels
Pagina's (van-tot)G870-G877
TijdschriftJournal of the Electrochemical Society
Volume151
Nummer van het tijdschrift12
DOI's
StatusGepubliceerd - 1 dec 2004
Extern gepubliceerdJa

Vingerafdruk

Duik in de onderzoeksthema's van 'Characterization of thermal and electrical stability of MOCVD HfO <sub>2</sub>-HfSiO<sub>4</sub> dielectric layers with polysilicon electrodes for advanced CMOS technologies'. Samen vormen ze een unieke vingerafdruk.

Citeer dit