Amorphous and perovskite Li3xLa(2/3)−xTiO3 (thin) films via chemical solution deposition: solid electrolytes for all-solid-state Li-ion batteries

E. J. van den Ham (Corresponding author), N. Peys, C. de Dobbelaere, J. D’Haen, F. Mattelaer, C. Detavernier, P. H.L. Notten, A. Hardy, M. K. Van Bael

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

9 Citaten (Scopus)

Samenvatting

Thin films of amorphous and crystalline perovskite Li3xLa(2/3)−xTiO3 (LLT) (x = 0.117) are prepared by means of aqueous chemical solution deposition onto rutile TiO2 thin films as an anode, yielding an electrochemical half-cell. The Li-ion conductivity of the pin-hole free, amorphous LLT thin film (90 nm thick) is 3.8 × 10−8 S cm−1 on Pt and 1.3 × 10−8 S cm−1 on rutile TiO2, while measuring perpendicular to the thin film direction with impedance spectroscopy. Grazing angle attenuated total reflectance-Fourier transform infrared spectroscopy shows that all organic precursor molecules have been decomposed at 500 °C. In addition, in situ (heating) X-ray diffraction analysis shows that phase pure crystalline perovskite LLT (x = 0.117) is formed on top of the rutile TiO2 anode at 700 °C. Furthermore, thickness control is possible by varying the precursor solution concentration and the number of deposition cycles. The current study presents a promising synthesis route to develop all-solid-state battery devices based on multi-metal oxide materials using aqueous precursor chemistry.

Originele taal-2Engels
Pagina's (van-tot)536-543
Aantal pagina's8
TijdschriftJournal of Sol-Gel Science and Technology
Volume73
Nummer van het tijdschrift3
DOI's
StatusGepubliceerd - 1 jan 2015

Vingerafdruk Duik in de onderzoeksthema's van 'Amorphous and perovskite Li<sub>3x</sub>La<sub>(2/3)−x</sub>TiO<sub>3</sub> (thin) films via chemical solution deposition: solid electrolytes for all-solid-state Li-ion batteries'. Samen vormen ze een unieke vingerafdruk.

  • Citeer dit