A simple and flexible route to large-area conductive transparent graphene thin-films

K. Arapov, A. Goryachev, G. With, de, H. Friedrich

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

11 Citaten (Scopus)
199 Downloads (Pure)

Samenvatting

Solution-processed conductive, flexible and transparent graphene thin films continue drawing attention from science and technology due to their potential for many electrical applications. Here, an up-scalable method for the solution processing of graphite to graphene and further to self-assembled large-area conductive transparent thin-films is presented. The method proceeds via the graphite intercalation route followed by thermal expansion to obtain expanded graphite. The resulting material is dispersed in a surfactant-free mixture of isopropanol and propylene glycol to obtain a stable colloidal dispersion. A graphene thin film is subsequently formed by self-organization at an oil/water interface followed by lift-up transfer to virtually any substrate of interest. Thermally annealed thin-films exhibit a thickness-tunable sheet resistances of between 10 and 0.8 kO/¿ with transparencies between 75% and 45% at 500 nm wavelength, respectively. Additional Au-doping decreases the sheet resistance by a factor of 5. Heating doped films to temperatures above 380 K or exposure to ambient conditions significantly increases the sheet resistance as a result of decreasing charge carrier concentration. The presented method is a simple, up-scalable and thus competitive alternative to other techniques for large area graphene film production.
Originele taal-2Engels
Pagina's (van-tot)67-75
Aantal pagina's9
TijdschriftSynthetic Metals
Volume201
DOI's
StatusGepubliceerd - 2015

Vingerafdruk Duik in de onderzoeksthema's van 'A simple and flexible route to large-area conductive transparent graphene thin-films'. Samen vormen ze een unieke vingerafdruk.

  • Uitrusting

    Center for Multiscale Electron Microscopy (CMEM)

    Heiner Friedrich (Manager), Rick Joosten (Gebruiker), Demi de Moor (Gebruiker), Pauline Schmit (Gebruiker), Ingeborg Schreur - Piet (Gebruiker), Anne Spoelstra (Gebruiker) & Nina Romme - van Moll (Inhoud)

    Materials and Interface Chemistry

    Uitrusting/faciliteit: Onderzoekslaboratorium

  • Citeer dit