A Mössbauer study of Al and Ga substituted magnetite

M. Rosenberg, P. Deppe, H.U. Janssen, V.A.M. Brabers, F.S. Li, S. Dey

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

29 Citaten (Scopus)
160 Downloads (Pure)


A Mössbauer study of Fe3-xAlxO4 and Fe3-xGaxO4 has been undertaken. Measurements at low temperatures in magnetic fields enabled us to better separate the Fe(A) and Fe(B) subspectra and to determine the cation distribution on tetrahedral and octahedral sites. Whereas Al up to x=1.4 shows a strong preference for B sites, giving rise to a normalization of the spinel structure with Fe2+ located mainly in tetrahedral sites, Ga distributes over both A and B places without tendency towards normalization at least below x¿1.2.
Originele taal-2Engels
Pagina's (van-tot)3740-3742
Aantal pagina's3
TijdschriftJournal of Applied Physics
Nummer van het tijdschrift8
StatusGepubliceerd - 1985


Duik in de onderzoeksthema's van 'A Mössbauer study of Al and Ga substituted magnetite'. Samen vormen ze een unieke vingerafdruk.

Citeer dit