A computational model for chemo-mechanical degradation of historical oil paintings due to metal soap formation

Gijs Eumelen, Emanuela Bosco (Corresponding author), Akke S.J. Suiker, Annelies van Loon, Piet Iedema

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

Uittreksel

A large percentage of oil paintings in museum collections suffers from chemo-mechanical degradation phenomena that are primarily due to metal soap formation. Metal soaps result from the chemical reaction between metal ions present in the pigments and saturated fatty acids released by the oil paint. They appear as large protrusions that disfigure the surface texture, possibly triggering mechanical damage and flaking of the painting. Despite that these phenomena have been widely observed in situ, the interaction between chemical and mechanical degradation processes is far from being understood. This paper proposes a chemo-mechanical model to predict metal soap formation and the resulting chemo-mechanical damage in historical oil paintings. The chemical process is described by means of a diffusion-reaction model, whereby the spatial growth of the metal soap crystal takes place in a small reaction zone at the boundary of the crystal. Metal soap crystallization and growth, driven by the diffusion of saturated fatty acids and metal ions, result in a chemically-induced volumetric growth strain. This introduces stresses in the paint, ultimately promoting crack nucleation and propagation. The fracture process is simulated with a cohesive zone approach, using interface elements equipped with a traction-separation law. The mass flux-concentration relation at the interfaces is consistently specified as a function of the mechanical damage. A set of numerical simulations illustrates the capability of the model to predict metal soap crystallization and growth and the fracture induced in the paint. The study finally illustrates the influence of various chemical and mechanical parameters (i.e., the size of the metal soap nucleus, the mismatch in elastic stiffness parameters between the metal soap and paint materials, the fracture length scale of the paint material, the chemical growth strain and the reaction rate) on the chemo-mechanical degradation of the paint layer.
TaalEngels
Artikelnummer103683
Aantal pagina's21
TijdschriftJournal of the Mechanics and Physics of Solids
Volume132
DOI's
StatusGepubliceerd - 1 nov 2019

Vingerafdruk

soaps
Soaps (detergents)
Painting
paints
oils
Paint
degradation
Degradation
Metals
metals
Saturated fatty acids
fatty acids
damage
Metal ions
metal ions
Crystallization
flaking
crystallization
museums
Crystals

Citeer dit

@article{3f76c8250cda42fd94491b931271bc47,
title = "A computational model for chemo-mechanical degradation of historical oil paintings due to metal soap formation",
abstract = "A large percentage of oil paintings in museum collections suffers from chemo-mechanical degradation phenomena that are primarily due to metal soap formation. Metal soaps result from the chemical reaction between metal ions present in the pigments and saturated fatty acids released by the oil paint. They appear as large protrusions that disfigure the surface texture, possibly triggering mechanical damage and flaking of the painting. Despite that these phenomena have been widely observed in situ, the interaction between chemical and mechanical degradation processes is far from being understood. This paper proposes a chemo-mechanical model to predict metal soap formation and the resulting chemo-mechanical damage in historical oil paintings. The chemical process is described by means of a diffusion-reaction model, whereby the spatial growth of the metal soap crystal takes place in a small reaction zone at the boundary of the crystal. Metal soap crystallization and growth, driven by the diffusion of saturated fatty acids and metal ions, result in a chemically-induced volumetric growth strain. This introduces stresses in the paint, ultimately promoting crack nucleation and propagation. The fracture process is simulated with a cohesive zone approach, using interface elements equipped with a traction-separation law. The mass flux-concentration relation at the interfaces is consistently specified as a function of the mechanical damage. A set of numerical simulations illustrates the capability of the model to predict metal soap crystallization and growth and the fracture induced in the paint. The study finally illustrates the influence of various chemical and mechanical parameters (i.e., the size of the metal soap nucleus, the mismatch in elastic stiffness parameters between the metal soap and paint materials, the fracture length scale of the paint material, the chemical growth strain and the reaction rate) on the chemo-mechanical degradation of the paint layer.",
author = "Gijs Eumelen and Emanuela Bosco and Suiker, {Akke S.J.} and {van Loon}, Annelies and Piet Iedema",
year = "2019",
month = "11",
day = "1",
doi = "10.1016/j.jmps.2019.103683",
language = "English",
volume = "132",
journal = "Journal of the Mechanics and Physics of Solids",
issn = "0022-5096",
publisher = "Elsevier",

}

A computational model for chemo-mechanical degradation of historical oil paintings due to metal soap formation. / Eumelen, Gijs; Bosco, Emanuela (Corresponding author); Suiker, Akke S.J.; van Loon, Annelies; Iedema, Piet.

In: Journal of the Mechanics and Physics of Solids, Vol. 132, 103683, 01.11.2019.

Onderzoeksoutput: Bijdrage aan tijdschriftTijdschriftartikelAcademicpeer review

TY - JOUR

T1 - A computational model for chemo-mechanical degradation of historical oil paintings due to metal soap formation

AU - Eumelen,Gijs

AU - Bosco,Emanuela

AU - Suiker,Akke S.J.

AU - van Loon,Annelies

AU - Iedema,Piet

PY - 2019/11/1

Y1 - 2019/11/1

N2 - A large percentage of oil paintings in museum collections suffers from chemo-mechanical degradation phenomena that are primarily due to metal soap formation. Metal soaps result from the chemical reaction between metal ions present in the pigments and saturated fatty acids released by the oil paint. They appear as large protrusions that disfigure the surface texture, possibly triggering mechanical damage and flaking of the painting. Despite that these phenomena have been widely observed in situ, the interaction between chemical and mechanical degradation processes is far from being understood. This paper proposes a chemo-mechanical model to predict metal soap formation and the resulting chemo-mechanical damage in historical oil paintings. The chemical process is described by means of a diffusion-reaction model, whereby the spatial growth of the metal soap crystal takes place in a small reaction zone at the boundary of the crystal. Metal soap crystallization and growth, driven by the diffusion of saturated fatty acids and metal ions, result in a chemically-induced volumetric growth strain. This introduces stresses in the paint, ultimately promoting crack nucleation and propagation. The fracture process is simulated with a cohesive zone approach, using interface elements equipped with a traction-separation law. The mass flux-concentration relation at the interfaces is consistently specified as a function of the mechanical damage. A set of numerical simulations illustrates the capability of the model to predict metal soap crystallization and growth and the fracture induced in the paint. The study finally illustrates the influence of various chemical and mechanical parameters (i.e., the size of the metal soap nucleus, the mismatch in elastic stiffness parameters between the metal soap and paint materials, the fracture length scale of the paint material, the chemical growth strain and the reaction rate) on the chemo-mechanical degradation of the paint layer.

AB - A large percentage of oil paintings in museum collections suffers from chemo-mechanical degradation phenomena that are primarily due to metal soap formation. Metal soaps result from the chemical reaction between metal ions present in the pigments and saturated fatty acids released by the oil paint. They appear as large protrusions that disfigure the surface texture, possibly triggering mechanical damage and flaking of the painting. Despite that these phenomena have been widely observed in situ, the interaction between chemical and mechanical degradation processes is far from being understood. This paper proposes a chemo-mechanical model to predict metal soap formation and the resulting chemo-mechanical damage in historical oil paintings. The chemical process is described by means of a diffusion-reaction model, whereby the spatial growth of the metal soap crystal takes place in a small reaction zone at the boundary of the crystal. Metal soap crystallization and growth, driven by the diffusion of saturated fatty acids and metal ions, result in a chemically-induced volumetric growth strain. This introduces stresses in the paint, ultimately promoting crack nucleation and propagation. The fracture process is simulated with a cohesive zone approach, using interface elements equipped with a traction-separation law. The mass flux-concentration relation at the interfaces is consistently specified as a function of the mechanical damage. A set of numerical simulations illustrates the capability of the model to predict metal soap crystallization and growth and the fracture induced in the paint. The study finally illustrates the influence of various chemical and mechanical parameters (i.e., the size of the metal soap nucleus, the mismatch in elastic stiffness parameters between the metal soap and paint materials, the fracture length scale of the paint material, the chemical growth strain and the reaction rate) on the chemo-mechanical degradation of the paint layer.

U2 - 10.1016/j.jmps.2019.103683

DO - 10.1016/j.jmps.2019.103683

M3 - Article

VL - 132

JO - Journal of the Mechanics and Physics of Solids

T2 - Journal of the Mechanics and Physics of Solids

JF - Journal of the Mechanics and Physics of Solids

SN - 0022-5096

M1 - 103683

ER -