Abstract
The dependence of the lattice parameter of g-aluminum oxynitride (Alon) on its compn. was investigated. The width of the homogeneity of Alon varies with temp.: at 1850 Deg Alon is the stable phase between 66 mol% Al2O3 (lattice parameter 0.7953 nm) and 81 mol% Al2O3 (lattice parameter 0.7932 nm). This region becomes smaller at lower temps. At