Synthesis and characterization of hydroxyl end-capped telechelic polymers with poly(methyl methacrylate)-block-poly(n-butyl acrylate) backbones via atomtransfer radical polymerization

Hydroxyl end-capped telechelic polymers with poly(methyl methacrylate)-block-poly(n-butyl acrylate) (PMMA-b-PBA) backbones have been prepared via atom transfer radical polymerisation (ATRP) together with a nucleophilic substitution reaction. A hydroxyl-functionalised PMMA macroinitiator (HO-PMMA-Br) was prepared via ATRP at the optimised reaction temperature (60 °C) using 2-hydroxyethyl 2-bromoisobutyrate as the initiator. The high functionality of the bromo end group in the macroinitiator was confirmed by both 1H NMR technique and a chain-extension reaction. Electrospray ionisation mass spectrometer proved to be a valuable tool for characterising PMMAs with a bromo end group (PMMA-Br), which provided signals corresponding to the intact polymers although multiply charged polymer chains were observed. The well-defined block copolymers HO-PMMA-b-PBA-Br were obtained by the ATRP of n-butyl acrylate using HO-PMMA-Br as a macroinitiator in a one-pot reaction at 100 °C. The kinetics as well as the dependence of the Mn,SEC and PDIs of the obtained block copolymers on the conversions of n-butyl acrylate in the chain-extension reaction suggested negligible radical termination during the reaction, demonstrating that the well-defined HO-PMMA-b-PBA-Br with a high functionality of bromo end group were obtained. The nucleophilic substitution reaction of a monohydroxyl-functionalised block copolymer HO-PMMA-b-PBA-Br with 5-amino-1-pentanol in dimethyl sulfoxide at room temperature was verified with 1H and 13C NMR techniques, which resulted in a series of telechelic polymers HO-PMMA-b-PBA-OH with a functionality of hydroxyl groups up to 1.7 according to the gradient polymer elution chromatography.