Abstract
The isothermal cross section through the ternary phase diagram Ga-P-Co at 500 °C was constructed. No ternary phases exist in the system at this temperature. All binary Co-P and Co-Ga intermetallics are in equilibrium with GaP, which, under these conditions, dissolves up to 4 at.% of cobalt. The use of equilibrium phase diagram information in predicting the variation of chemical composition in the diffusion zone during solid-state reaction between GaP and Co is demonstrated.
Original language | English |
---|---|
Pages (from-to) | 227-231 |
Journal | Journal of Phase Equilibria |
Volume | 22 |
Issue number | 3 |
DOIs | |
Publication status | Published - 2001 |