Abstract
A new compd. (G1) consisting of 18.5-23.5 at. % Fe and the rest Zn was found in the Fe-Zn system at 380 Deg by the diffusion-couple technique. The lattice of this compd. is related to that of the G phase and its lattice parameter (17.963 .ANG.) is obtained by doubling that of the bcc. unit cell of the G phase. But the new cell is fcc. The homogeneity range of G1 decreases with increasing temp. whereas the reverse was obsd. for the G phase. Based on these facts, a modified phase diagram is proposed. [on SciFinder (R)]
| Original language | English |
|---|---|
| Pages (from-to) | 656-660 |
| Number of pages | 5 |
| Journal | Zeitschrift fuer Metallkunde |
| Volume | 65 |
| Issue number | 10 |
| Publication status | Published - 1974 |