Growth and electrical properties of zirconium-zinc (ZrZn2) single crystals

L.W.M. Schreurs; H.M. Weijers; A.P.J. Deursen, van; A.R. Vroomen, De

doi:10.1016/0025-5408(89)90072-X

Growth and electrical properties of zirconium-zinc (ZrZn2) single crystals

L.W.M. Schreurs
, H.M. Weijers
, A.P.J. Deursen, van
, A.R. Vroomen, De

Research output: Contribution to journal › Article › Academic › peer-review

16 Citations (Scopus)

2 Downloads (Pure)

Abstract

A method for growing ZrZn2 crystals from the melt is described. In a 1 cm3 sample, which contains large crystals, we measured very high resistivity ratios 293K / 4.2K of 120–131. The lattice constant was 0.73969(5)nm and the zinc-zirconium ratio 1.99. The temperature dependence of the resistivity was also measured. Furthermore, the crystals were characterized by Curie temperature and magnetic moment measurements.

Original language	English
Pages (from-to)	1141-1145
Number of pages	5
Journal	Materials Research Bulletin
Volume	24
Issue number	9
DOIs	https://doi.org/10.1016/0025-5408(89)90072-X
Publication status	Published - 1989

Access to Document

10.1016/0025-5408(89)90072-X

Cite this

@article{c151df4d637547159e2e6baf198eadcf,

title = "Growth and electrical properties of zirconium-zinc (ZrZn2) single crystals",

abstract = "A method for growing ZrZn2 crystals from the melt is described. In a 1 cm3 sample, which contains large crystals, we measured very high resistivity ratios 293K / 4.2K of 120{\textendash}131. The lattice constant was 0.73969(5)nm and the zinc-zirconium ratio 1.99. The temperature dependence of the resistivity was also measured. Furthermore, the crystals were characterized by Curie temperature and magnetic moment measurements.",

author = "L.W.M. Schreurs and H.M. Weijers and \{Deursen, van\}, A.P.J. and \{Vroomen, De\}, A.R.",

year = "1989",

doi = "10.1016/0025-5408(89)90072-X",

language = "English",

volume = "24",

pages = "1141--1145",

journal = "Materials Research Bulletin",

issn = "0025-5408",

publisher = "Elsevier",

number = "9",

}

TY - JOUR

T1 - Growth and electrical properties of zirconium-zinc (ZrZn2) single crystals

AU - Schreurs, L.W.M.

AU - Weijers, H.M.

AU - Deursen, van, A.P.J.

AU - Vroomen, De, A.R.

PY - 1989

Y1 - 1989

N2 - A method for growing ZrZn2 crystals from the melt is described. In a 1 cm3 sample, which contains large crystals, we measured very high resistivity ratios 293K / 4.2K of 120–131. The lattice constant was 0.73969(5)nm and the zinc-zirconium ratio 1.99. The temperature dependence of the resistivity was also measured. Furthermore, the crystals were characterized by Curie temperature and magnetic moment measurements.

AB - A method for growing ZrZn2 crystals from the melt is described. In a 1 cm3 sample, which contains large crystals, we measured very high resistivity ratios 293K / 4.2K of 120–131. The lattice constant was 0.73969(5)nm and the zinc-zirconium ratio 1.99. The temperature dependence of the resistivity was also measured. Furthermore, the crystals were characterized by Curie temperature and magnetic moment measurements.

U2 - 10.1016/0025-5408(89)90072-X

DO - 10.1016/0025-5408(89)90072-X

M3 - Article

SN - 0025-5408

VL - 24

SP - 1141

EP - 1145

JO - Materials Research Bulletin

JF - Materials Research Bulletin

IS - 9

ER -

Growth and electrical properties of zirconium-zinc (ZrZn2) single crystals

Abstract

Access to Document

Fingerprint

Cite this